| About |
|---|
| LNP* Lubricomp* UFL36SX是以聚邻苯二甲酰胺为基体，含有玻璃纤维和PETF的树脂。此材料主要优势是具有内部润滑功能和热稳定性好。 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Hardness,High Heat Resistance,Lubricating,Heat Stabilized |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | 2000 | kgf/cm² | ASTM D 638 |
| fracture | 196 | MPa | ISO 527 |
| Tensile strain | |||
| fracture | 2.5 | % | ISO 527 |
| fracture | 2.5 | % | ASTM D638 |
| bending strength | 275.661 | MPa | ASTM D790 |
| Bending modulus | 10820.43 | MPa | ASTM D790 |
| Tensile modulus | |||
| 50 mm/min | 12409.65 | MPa | ASTM D638 |
| 1 mm/min | 9880 | MPa | ISO 527 |
| bending strength | 286 | MPa | ISO 178 |
| Bending modulus | 11230 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃，80*10*4 | 70 | kJ/m² | ISO 180/1U |
| 23℃ | 1009.4 | J/m | ASTM D4812 |
| Impact strength of cantilever beam notch | |||
| 23℃，80*10*4 | 12 | kJ/m² | ISO 180-1A |
| 23℃ | 107.8 | J/m | ASTM D256 |
| Instrument impact energy peak | |||
| 23℃ | 71 | cm-kgf | ASTM D 3763 |
| Multiaxial impact | 30 | cm-kgf | ISO 6603 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 260 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 255 | ℃ | ISO 75/Af |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 24hr，50% RH | 0.3 | % | ASTM D570 |
| Shrinkage rate | 0.2 | % | ASTM D 955 |
| MD：24 hrs | 0.82 | % | ISO 294 |
| MD：24 hrs | 0.17 | % | ISO 294 |
| MD：24 hrs | 0.8 | % | ASTM D955 |
| Factors of gasket wear | 6 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified |
| friction coefficient | |||
| dynamic | 0.46 | ASTM D3702 | |
| friction coefficient | |||
| static state | 0.49 | ASTM D3702 | |
| Density | 1.55 | g/cm³ | ISO 1183 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Drying temperature | 120 | ℃ | |
| Drying time | 4 | hrs | |
| Maximum water content | 0.15 | % | |
| Melt temperature | 315-330 | ℃ | |
| Front temperature | 325-340 | ℃ | |
| Mid section temperature | 315-325 | ℃ | |
| Post stage temperature | 310-320 | ℃ | |
| Mold temperature | 150-170 | ℃ | |
| Back pressure | 0.2-0.3 | MPa | |
| Screw speed | 30-60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |