| About |
|---|
| LNP LUBRICOMP UX06425 is a compound based on Polyphthalamide (PPA) containing 10% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Hot Water Moldable and Heat Stabilized. Also known as: LNP* LUBRICOMP* Compound UFL-4022 A HS HW Product reorder name: UX06425&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Lubricating,Good wear resistance,Heat Stabilized |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：24 hrs | 0.70-0.90 | % | ASTM D995 |
| TD：24 hrs | 1.0-3.0 | % | ASTM D995 |
| Water absorption rate | |||
| 23℃，50% RH | 0.31 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 89 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 1.5 | % | ASTM D638 |
| Tensile modulus | |||
| 23℃ | 6610 | MPa | ASTM D638 |
| bending strength | |||
| 23℃ | 132 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 5710 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 293 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 260 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 4.1E-5 | 1/℃ | ASTM D696 |
| TD | 7.5E-5 | 1/℃ | ASTM D696 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 33 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 200 | J/m | ASTM D4812 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4 | Hr | |
| Water content | 0.060 | % | |
| Injection temperature | |||
| Rear barrel temperature | 315-325 | °C | |
| Central temperature of the barrel | 325-330 | °C | |
| Barrel front temperature | 330-345 | °C | |
| Mold temperature | 65-95 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |