| About |
|---|
| LNP LUBRICOMP VN001 is a compound based on Super Tough Nylon containing 2% MOS2. Added feature of th is grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound VL-4210 D Product reorder name: VN001&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA Not specified |
| Material Status | Commercial: Active |
| Features | Lubricating,Good wear resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ASTM D792 |
| Density | 1.10 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD：24 hrs | 2.0 to 5.0 | % | ASTM D955 |
| MD：24 hrs | 2.0 to 5.0 | % | ASTM D955 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 1.1 | % | ISO 62 |
| 24hr，50% RH | 0.80 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2290 | MPa | ASTM D638 |
| Tensile modulus | 2390 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 48.3 | MPa | ASTM D638 |
| fracture | 53.8 | MPa | ISO 527-2/5 |
| yield | 56.4 | MPa | ISO 527-2/5 |
| yield | 53.9 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 41 | % | ASTM D638 |
| fracture | 28 | % | ISO 527-2/5 |
| yield | 38 | % | ASTM D638 |
| yield | 5.3 | % | ISO 527-2/5 |
| Bending modulus | 2080 | MPa | ISO 178 |
| 50 mm span | 1910 | MPa | ASTM D790 |
| bending strength | 69.6 | MPa | ISO 178 |
| friction coefficient | ASTM D3702 Modified | ||
| dynamic | 0.79 | ASTM D3702 Modified | |
| static state | 0.36 | ASTM D3702 Modified | |
| Fracture bending strain | 4.0 | % | ISO 178 |
| Wear factor | |||
| Washer | 71.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 1700 | J/m | ASTM D4812 |
| 23℃ | 160 | J/m | ASTM D256 |
| 23℃ | 16 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 180 | kJ/m² | ISO 180/1U |
| Multi axial instrumented impact energy | 22.3 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 64.0 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 65.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 210 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 216 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-30~30℃ | 1.2E-4 | 1/℃ | ASTM D696 |
| MD：-30~30℃ | 1.2E-4 | 1/℃ | ASTM D696 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Barrel rear temperature | 260 to 271 | °C | |
| Barrel middle temperature | 277 to 288 | °C | |
| Barrel front temperature | 293 to 304 | °C | |
| Processing (melt) temperature | 282 to 293 | °C | |
| Mold temperature | 93 to 110 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |