| About |
|---|
| LNP LUBRICOMP XFL36 is a compound based on Amorphous Nylon containing 30% Glass Fiber and 15% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound XFL-4036 Product reorder name: XFL36&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA Not specified |
| Material Status | Commercial: Active |
| Features | Lubricating,Good wear resistance,Amorphous |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.47 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 24hr，50% RH | 0.15 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 127 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.0 to 4.0 | % | ASTM D638 |
| Bending modulus | |||
| 50 mm span | 7930 | MPa | ASTM D790 |
| bending strength | |||
| Fracture, 50 mm span | 172 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 270 | J/m | ASTM D4812 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 137 | ℃ | ASTM D648 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 120 | °C | |
| Drying time | 6.0 to 12 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Barrel rear temperature | 260 to 270 | °C | |
| Barrel middle temperature | 270 to 290 | °C | |
| Barrel front temperature | 290 to 300 | °C | |
| Processing (melt) temperature | 260 to 300 | °C | |
| Mold temperature | 50 to 100 | °C | |
| Back pressure | 0.170 to 0.340 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |