| About |
|---|
| LNP LUBRICOMP* ZFL34XXC是的PPE和PPS的混合树脂，用玻璃纤维和PTFE进行了改性处理。此材料有内部润滑功能。 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good Dimensional Stability,Flame Characteristics,High Heat Resistance,Insulation |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | 87 | MPa | ASTM D 638 |
| Tensile strain | 1.8 | % | ASTM D638 |
| bending strength | 132.435 | MPa | ASTM D790 |
| Bending modulus | 6749.28 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃ | 333.2 | J/m | ASTM D4812 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 58.8 | J/m | ASTM D256 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.3 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：24 hrs | 0.5 | % | ASTM D955 |
| MD：24 hrs | 0.3 | % | ASTM D955 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 131 | ℃ | ASTM D648 |
| drying temperature | 120 | ℃ | |
| drying time | 4 | hrs | |
| Melt Temperature | 300-305 | ℃ | |
| Front temperature | 300-310 | ℃ | |
| Mid section temperature | 290-300 | ℃ | |
| Post stage temperature | 275-290 | ℃ | |
| Mold temperature | 80-100 | ℃ | |
| Back pressure | 0.2-0.3 | MPa | |
| Screw speed | 30-60 | rpm |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |