| About |
|---|
| LNP LUBRILOY ZX06315 is a compound based on PPE+PS Blend resin containing Flame Retardant, Proprietary Lubricant. Added features of this material include: Internally Lubricated, Non-Brominated u0026amp; Non-Chlorinated Flame Retardant, Flame Retardant, high HDT. |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+SEBS+Polyolefin |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,Lubricating |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ASTM D792 |
| Melt Volume Rate | |||
| 280℃，10 kg | 38.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：24 hrs | 0.94 to 0.96 | % | |
| TD：24 hrs | 0.91 to 0.93 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 230 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 124 | ℃ | |
| 1.8 MPa, unannealed, 6.4 mm | 129 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 7.2E-4 | 1/℃ | |
| TD：-40~40℃ | 8.6E-4 | 1/℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-1 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 115 | ASTM D785 | |
| Tensile modulus | 2270 | MPa | ASTM D638 |
| Tensile strength | |||
| yield | 63.0 | MPa | |
| fracture | 50.0 | MPa | |
| Tensile strain | |||
| yield | 5.0 | % | |
| fracture | 12 | % | |
| Bending modulus | |||
| 50 mm span | 2190 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 93.0 | MPa | |
| Fracture, 50 mm span | 91.0 | MPa | |
| friction coefficient | |||
| dynamic | 0.21 | ASTM D3702 | |
| Wear factor | 1.3E+7 | 10^-8 mm³/N·m | ASTM D3702 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Temperature at the rear of the barrel | 265 to 60255 | °C | |
| Temperature in the middle of the barrel | 260 to 270 | °C | |
| Front temperature of material barrel | 265 to 275 | °C | |
| Nozzle temperature | 265 to 275 | °C | |
| Processing (melt) temperature | 270 to 295 | °C | |
| Mold temperature | 60 to 95 | °C | |
| Back pressure | 0.200 to 0.400 | MPa | |
| Screw speed | 40 to 100 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |