| About |
|---|
| LNP LUBRILOY* D20001 is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Flame Retardant. Wear Resistant.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Lubricating,Good wear resistance,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 0.60 | % | ASTM D955 |
| MD：24 hrs | 0.50 | % | ASTM D955 |
| TD：24 hrs | 0.57 | % | ISO 294-4 |
| MD：24 hrs | 0.53 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.12 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2550 | MPa | ASTM D638 |
| Tensile modulus | 2600 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 60.2 | MPa | ASTM D638 |
| fracture | 54.5 | MPa | ISO 527-2 |
| yield | 67.3 | MPa | ASTM D638 |
| yield | 62.3 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 6.5 | % | ASTM D638 |
| fracture | 6.7 | % | ISO 527-2 |
| yield | 4.3 | % | ISO 527-2 |
| yield | 4.5 | % | ASTM D638 |
| Bending modulus | 2830 | MPa | ASTM D790 |
| Bending modulus | 2800 | MPa | ISO 178 |
| bending strength | 103 | MPa | ASTM D790 |
| bending strength | 102 | MPa | ISO 178 |
| friction coefficient | ASTM D3702 Modified | ||
| dynamic | 0.29 | ASTM D3702 Modified | |
| static state | 0.16 | ASTM D3702 Modified | |
| Wear factor | |||
| Washer | 10.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 6.9 | kJ/m² | ISO 180-1A |
| 23℃ | 64 | J/m | ASTM D256 |
| 23℃ | 1600 | J/m | ASTM D4812 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 100 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 51.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 94.0 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 89.4 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 97.2 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 6.7E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 6.7E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 6.6E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 6.6E-5 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 249 to 260 | °C | |
| Barrel middle temperature | 254 to 266 | °C | |
| Barrel front temperature | 260 to 271 | °C | |
| Processing (melt) temperature | 254 to 288 | °C | |
| Mold temperature | 38 to 66 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type 1A |
| 4. Modified: Manual |
| 5. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |