| About |
|---|
| LNP STAT-KON* 9X02785 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Conductive |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.27 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：24 hrs | 0.40-0.70 | % | ASTM D995 |
| TD：24 hrs | 0.50-0.80 | % | ASTM D995 |
| Water absorption rate | |||
| 23℃，50% RH | 0.091 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 64 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 4 | % | ASTM D638 |
| Tensile modulus | |||
| 23℃ | 2850 | MPa | ASTM D638 |
| bending strength | |||
| 23℃ | 103 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 2920 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 117 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 106 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 6.8E-5 | 1/℃ | ASTM D696 |
| TD | 6.8E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+3 | Ω.cm | ASTM D257 |
| Surface resistance | 1.0E+5 | Ω.cm | ASTM D257 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 60 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 2200 | J/m | ASTM D256 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 4.0 | Hr | |
| Water content | 0.020 | % | |
| Injection temperature | |||
| Rear barrel temperature | 295-305 | °C | |
| Central temperature of the barrel | 310-320 | °C | |
| Barrel front temperature | 320-330 | °C | |
| Mold temperature | 80-110 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. Type 1A |
| 7. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |