| About |
|---|
| LNP* STAT-KON* AE003 is a compound based on ABS containing 15% Carbon Fiber. Added feature of this grade is: Electrically Conductive.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Conductive |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| TD：24 hrs | 0.55 | % | ASTM D955 |
| MD：24 hrs | 0.10 | % | ASTM D955 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.28 | % | ISO 62 |
| 24hr，50% RH | 0.19 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 12800 | MPa | ASTM D638 |
| Tensile modulus | 11500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 93.0 | MPa | ISO 527-2/5 |
| fracture | 92.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 0.90 | % | ASTM D638 |
| fracture | 0.90 | % | ISO 527-2/5 |
| Bending modulus | 12300 | MPa | ISO 178 |
| 50 mm span | 12600 | MPa | ASTM D790 |
| bending strength | 119 | MPa | ISO 178 |
| Fracture, 50 mm span | 95.0 | MPa | ASTM D790 |
| Yield, 50 mm span | 114 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 270 | J/m | ASTM D4812 |
| 23℃ | 5.7 | kJ/m² | ISO 180-1A |
| 23℃ | 60 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 16 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 7.10 | J | ASTM D3763 |
| Multi axial instrumented impact energy | 2.18 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 104 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 102 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 104 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 105 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-30~30℃ | 6.6E-5 | 1/℃ | ASTM D696 |
| MD：-30~30℃ | 1.9E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 2.0 to 4.0 | ohms | ASTM D257 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.050 to 0.10 | % | |
| Barrel rear temperature | 204 to 216 | °C | |
| Barrel middle temperature | 232 to 243 | °C | |
| Barrel front temperature | 266 to 277 | °C | |
| Processing (melt) temperature | 260 | °C | |
| Mold temperature | 71 to 82 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. at Yield |
| 4. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |