| About |
|---|
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics |
| Availabilitys | North America,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.050 to 0.15 | % | |
| TD：3.2 mm | 0.15 to 0.30 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 69 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 240 | J/m | ASTM D4812 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 111 | ℃ | |
| 1.8 MPa, unannealed, 6.4 mm | 105 | ℃ | |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.3E+4 | ohms | ASTM D257 |
| Volume resistivity | 8.0E+3 | ohms·cm | ASTM D257 |
| Static Decay – 5000V to <50V | < 10 | msec | FTMS 101B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 2.00 mm | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 122 | ASTM D785 | |
| Tensile strength | |||
| yield | 79.0 | MPa | |
| fracture | 71.0 | MPa | |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| Bending modulus | |||
| 100 mm span | 6890 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 100 mm span | 103 | MPa | ASTM D790 |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-17 wheels | 83.0 | mg | ASTM D1044 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 90 to 95 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Suggested injection volume | 30 to 70 | % | |
| Temperature at the rear of the barrel | 220 to 270 | °C | |
| Temperature in the middle of the barrel | 230 to 275 | °C | |
| Front temperature of material barrel | 245 to 280 | °C | |
| Nozzle temperature | 255 to 280 | °C | |
| Processing (melt) temperature | 255 to 280 | °C | |
| Mold temperature | 65 to 90 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Exhaust hole depth | 0.038 to 0.051 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |