LNP™ STAT-KON™ Compound ZX05009

About

Product Description
SupplierSABIC
GenericPPO(PPE)+PS
Material StatusCommercial: Active

Technical Data
MECHANICALNominal valueUnitTest method
tensile strength
Fracture, 5mm/min81MPaISO 527
Tensile strain
Fracture, 5mm/min1%ISO 527
Tensile modulus
1mm/min10000MPaISO 527
bending strength
Fracture, 2mm/min101MPaISO 178
Bending modulus
2mm/min7600MPaISO 178

IMPACTNominal valueUnitTest method
Notched impact strength of cantilever beam
80*10*4 sp=64mm10KJ/m²ISO 180/1U
Impact strength of cantilever beam notch
80*10*4 sp=64mm5KJ/m²ISO 180/1A

THERMALNominal valueUnitTest method
Hot deformation temperature
0.45 MPa141ISO 75/Bf
1.8 MPa135ISO 75/Af

PHYSICALNominal valueUnitTest method
Shrinkage rate0.2-0.4%ISO 294
Density1.15g/cm³ISO 1183

Electrical performanceNominal valueUnitTest method
Surface resistivity1.E+02 to 1.E+03ohmsASTM D257

Process Conditions
injection moldingNominal valueUnitTest method
drying temperature120
Drying time4hrs
Melt Temperature300-305
Temperature at the rear of the melt300-310
Temperature in the middle of the melt290-300
Melt front temperature275-290
Mold temperature80-100
Back pressure0.2-0.3MPa
Spray speed30-60rpm

Notes
【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.