| About |
|---|
| LNP STAT-KON* DE0029EF is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Easy Molding. Flame Retardant, Electrically Conductive.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Conductive,Flame Characteristics |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.26 | g/cm³ | ASTM D792 |
| Density | 1.26 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 0.20 to 0.40 | % | ASTM D955 |
| MD：24 hrs | 0.10 to 0.30 | % | ASTM D955 |
| TD：24 hrs | 0.29 to 0.43 | % | ISO 294-4 |
| MD：24 hrs | 0.060 to 0.32 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| 24hr，50% RH | 0.16 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 8890 | MPa | ASTM D638 |
| Tensile modulus | 8500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 117 | MPa | ISO 527-2 |
| fracture | 114 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.3 | % | ASTM D638 |
| fracture | 2.4 | % | ISO 527-2 |
| Bending modulus | 7650 | MPa | ASTM D790 |
| Bending modulus | 8800 | MPa | ISO 178 |
| bending strength | 181 | MPa | ASTM D790 |
| bending strength | 183 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 60 | J/m | ASTM D256 |
| 23℃ | 440 | J/m | ASTM D4812 |
| 23℃ | 6.9 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 30 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 17.1 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 139 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 141 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 144 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 3.5E-5 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 3.5E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 2.4E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 2.4E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 293 to 304 | °C | |
| Barrel middle temperature | 310 to 321 | °C | |
| Barrel front temperature | 321 to 332 | °C | |
| Processing (melt) temperature | 304 to 327 | °C | |
| Mold temperature | 82 to 110 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type 1A |
| 4. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |