| About |
|---|
| LNP Stat-Kon DX02437 is a compound based on Polycarbonate resin containing conductive carbon powder, with good impact-resistance, flow and ESD performance, suitable for semi-con industry.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High impact resistance,Conductive,Good liquidity,Electrostatic discharge protection |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | ASTM D792 |
| Melt Volume Rate | |||
| 300℃，5 kg | 16.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| MD | 0.64 | % | |
| TD | 0.68 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 2570 | MPa | ASTM D638 |
| — | 2550 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 58.0 | MPa | ASTM D638 |
| yield | 58.0 | MPa | ISO 527-2/5 |
| fracture | 47.0 | MPa | ASTM D638 |
| fracture | 47.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 19 | % | ASTM D638 |
| fracture | 17 | % | ISO 527-2/5 |
| Bending modulus | 2550 | MPa | ISO 178 |
| bending strength | ISO 178 | ||
| — | 92.0 | MPa | |
| — | 90.0 | MPa | |
| Fracture bending strain | 7.8 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 26 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 95 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 0℃ | 290 | J/m | ASTM D256 |
| 23℃ | 360 | J/m | ASTM D256 |
| 0℃ | 20 | kJ/m² | ISO 180-1A |
| 23℃ | 25 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 2100 | J/m | ASTM D4812 |
| 23℃ | 130 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 27.0 | J | ASTM D3763 |
| 23℃，Total Energy | 39.1 | J | ASTM D3763 |
| — | 63.1 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 111 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 126 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| A50 | 144 | ℃ | ASTM D1525，ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 4.8E+7 | ohms | ASTM D257 |
| Volume resistivity | 1.4E+7 | ohms·cm | ASTM D257 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 293 to 304 | °C | |
| Barrel middle temperature | 310 to 321 | °C | |
| Barrel front temperature | 321 to 332 | °C | |
| Processing (melt) temperature | 304 to 327 | °C | |
| Mold temperature | 82.2 to 110 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.079 in/min |
| 5. at Yield |
| 6. at Break |
| 7. 2 mm/min |
| 8. 80*10*4 sp=62mm |
| 9. 80*10*4 mm |
| 10. Rate A (50°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |