| About |
|---|
| LNP STAT-KON DX05301C is a compound based on Polycarbonate containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Conductive, Low Ionic, Low Outgassing, Low LPC and ESD safe. Suitable for Semiconductor and Hard Disk Drive (HDD) Applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Conductive,Low (to None) Ion Content,Electrostatic discharge protection,Low odor |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，5.0kg | 23 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 49 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 10 | % | ASTM D638 |
| Tensile modulus | |||
| 23℃ | 2600 | MPa | ASTM D638 |
| bending strength | |||
| 23℃ | 95 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 2280 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 132 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+5 to 1.0E+8 | Ω.cm | ASTM D257 |
| Surface resistance | 1.0E+5 to 1.0E+8 | Ω.cm | ASTM D257 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 54 | J/m | ASTM D256 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4 | Hr | |
| Water content | 0.02 | % | |
| Injection temperature | |||
| Rear barrel temperature | 295-305 | °C | |
| Central temperature of the barrel | 305-315 | °C | |
| Barrel front temperature | 310-320 | °C | |
| Die temperature | 310-320 | °C | |
| Mold temperature | 80-110 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |