| Low Ionic, Low Outgassing, Low LPC and ESD safe Polycarbonate compound suitable for Semiconductor and Hard Disk Drive (HDD) application.Added features of this material include: Clean Compounding System.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Low (to None) Ion Content,Electrostatic discharge protection,Low odor |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.22 | g/cm³ | ASTM D792 |
| — | 1.23 | g/cm³ | ISO 1183 |
| Shrinkage rate | ASTM D955 | ||
| MD：24 hrs | 0.50 to 0.70 | % | |
| TD：24 hrs | 0.50 to 0.70 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 2680 | MPa | ASTM D638 |
| — | 2600 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 64.9 | MPa | ASTM D638 |
| yield | 66.0 | MPa | ISO 527-2/5 |
| fracture | 51.7 | MPa | ASTM D638 |
| fracture | 54.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 5.4 | % | ASTM D638 |
| yield | 3.1 | % | ISO 527-2/5 |
| fracture | 15 | % | ASTM D638 |
| fracture | 12 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 2600 | MPa | ASTM D790 |
| — | 2560 | MPa | ISO 178 |
| bending strength | |||
| — | 99.0 | MPa | ISO 178 |
| Fracture, 50 mm span | 101 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 53 | J/m | ASTM D256 |
| 23℃ | 4.6 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 2200 | J/m | ASTM D4812 |
| 23℃ | 200 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 8.18 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 138 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 137 | ℃ | ISO 75-2/Af |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+3 to 1.0E+7 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+3 to 1.0E+7 | ohms·cm | ASTM D257 |
| Electrostatic attenuation | 0.1 | sec | FTMS 101B |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 295 to 305 | °C | |
| Barrel middle temperature | 310 to 320 | °C | |
| Barrel front temperature | 320 to 330 | °C | |
| Processing (melt) temperature | 305 to 325 | °C | |
| Mold temperature | 80.0 to 110 | °C | |
| Back pressure | 0.200 to 0.300 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |