| About |
|---|
| LNP STAT-KON* EE005E is a compound based on Polyetherimide resin containing 25% Carbon Fiber. Added features of this material include: Easy Molding, Electrically Conductive.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Conductive |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | ASTM D792 |
| Density | 1.36 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 0.30 to 0.50 | % | ASTM D955 |
| MD：24 hrs | 0.050 to 0.30 | % | ASTM D955 |
| TD：24 hrs | 0.30 to 0.50 | % | ISO 294-4 |
| MD：24 hrs | 0.10 to 0.30 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.23 | % | ISO 62 |
| 24hr，50% RH | 0.16 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 18300 | MPa | ASTM D638 |
| Tensile modulus | 18200 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 200 | MPa | ASTM D638 |
| fracture | 200 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 1.4 | % | ASTM D638 |
| fracture | 1.4 | % | ISO 527-2/5 |
| Bending modulus | 14300 | MPa | ASTM D790 |
| Bending modulus | 15000 | MPa | ISO 178 |
| bending strength | 278 | MPa | ASTM D790 |
| bending strength | 277 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 6.4 | kJ/m² | ISO 180-1A |
| 23℃ | 53 | J/m | ASTM D256 |
| 23℃ | 450 | J/m | ASTM D4812 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 30 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 10.4 | J | ASTM D3763 |
| Multi axial instrumented impact energy | 7.14 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 208 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 207 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 2.7E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 2.7E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 1.9E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 1.9E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+2 to 1.0E+5 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+2 to 1.0E+6 | ohms·cm | ASTM D257 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 to 149 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 343 to 354 | °C | |
| Barrel middle temperature | 354 to 366 | °C | |
| Barrel front temperature | 366 to 377 | °C | |
| Processing (melt) temperature | 360 to 366 | °C | |
| Mold temperature | 121 to 149 | °C | |
| Back pressure | 0.344 to 0.689 | MPa | |
| Screw speed | 60 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. Type 1A |
| 5. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |