| About |
|---|
| LNP STAT-KON EX11318C is a polyetherimide compound reinforced with carbon fiber for good stiffness, dimension stability and has extremely high level of cleanliness for the most demanding application. A unique feature of this material is its low C18-C40 hydrocarbons. This compound is manufactured using LNP CCS Technology.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Low (to None) Ion Content |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.39 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD：24 hrs | 0.10 to 0.20 | % | |
| TD：24 hrs | 0.15 to 0.25 | % | |
| Water absorption rate | |||
| 24hr，50% RH | 0.20 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 21800 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 211 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.9 | % | ASTM D638 |
| Bending modulus | |||
| 50 mm span | 18100 | MPa | ASTM D790 |
| bending strength | |||
| Fracture, 50 mm span | 270 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 48 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 380 | J/m | ASTM D4812 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 203 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~40℃ | 4.6E-6 | 1/℃ | |
| TD：-40~40℃ | 4.3E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 5.0E+3 to 5.0E+5 | ohms | ASTM D257 |
| Volume resistivity | 5.0E+3 to 5.0E+6 | ohms·cm | ASTM D257 |
| Electrostatic attenuation | 0.1 | sec | FTMS 101B |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 24 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |