| LNP STAT-KON NORYL_HMC1010 compound is a 10% Carbon fiber reinforced. Static dissipative. Nonbrominated, nonchlor- nated flame retardant system. UL94 V-1 rated.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.15 to 0.30 | % | Internal Method |
| MD：3.2 mm | 0.050 to 0.15 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 69 | J/m | ASTM D256 |
| 23℃ | 240 | J/m | ASTM D4812 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 105 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 111 | ℃ | ASTM D648 |
| Relative temperature index | |||
| Electrical performance | 50.0 | ℃ | UL 746 |
| Strength mechanical performance | 50.0 | ℃ | UL 746 |
| Impact mechanical performance | 50.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.3E+4 | ohms | ASTM D257 |
| Volume resistivity | 8.0E+3 | ohms·cm | ASTM D257 |
| Electrostatic attenuation | 10 | msec | FTMS 101B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 2.00 mm | V-1 5VA | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 71.0 | MPa | ASTM D638 |
| yield | 79.3 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| Bending modulus | |||
| 100 mm span | 6890 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 100 mm span | 103 | MPa | ASTM D790 |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-17 wheels | 83.0 | mg | ASTM D1044 |
| Rockwell hardness | |||
| R-level | 122 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 88 to 93 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 221 to 271 | °C | |
| Barrel middle temperature | 232 to 277 | °C | |
| Barrel front temperature | 243 to 282 | °C | |
| Nozzle temperature | 254 to 282 | °C | |
| Processing (melt) temperature | 254 to 282 | °C | |
| Mold temperature | 66 to 88 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Vent depth | 0.038 to 0.051 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 3. 0.10 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |