| PBT base, CF+Glass fiber filled, Halogen FR V-0, Low warpage&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Low warping,Flame Characteristics,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.54 | g/cm³ | ASTM D792 |
| Shrinkage rate | Internal Method | ||
| MD | 0.17 | % | |
| TD | 0.55 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 143 | MPa | Internal Method |
| Tensile strain | |||
| fracture | 9.0 | % | Internal Method |
| Bending modulus | |||
| 6.40 mm | 11600 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 6.40 mm | 208 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 78 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 205 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 9.0E+7 | ohms | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 2.00 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 12 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |