| About |
|---|
| LNP* STAT-KON* ZE004 is a compound based on PPO resin containing 20% Carbon Fiber. Added feature of this grade includes: Electrically Conductive.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE) |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
| Shrinkage rate | |||
| MD：24 hrs | 0.20 to 0.40 | % | ASTM D955 |
| TD：24 hrs | 0.40 to 0.60 | % | ASTM D955 |
| TD：24 hrs | 0.53 | % | ISO 294-4 |
| MD：24 hrs | 0.30 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 24800 | MPa | ASTM D638 |
| — | 14700 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 80.7 | MPa | ASTM D638 |
| yield | 54.0 | MPa | ISO 527-2 |
| fracture | 104 | MPa | ASTM D638 |
| fracture | 103 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 0.50 | % | ASTM D638 |
| fracture | 0.96 | % | ISO 527-2 |
| Bending modulus | |||
| — | 24100 | MPa | ASTM D790 |
| — | 12700 | MPa | ISO 178 |
| bending strength | |||
| — | 179 | MPa | ASTM D790 |
| — | 151 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 37 | J/m | ASTM D256 |
| 23℃ | 4.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 300 | J/m | ASTM D4812 |
| 23℃ | 18 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 139 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 141 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.2 mm | 137 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 135 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 4.9E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 4.8E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 3.6E-5 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 3.7E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 277 to 288 | °C | |
| Barrel middle temperature | 288 to 299 | °C | |
| Barrel front temperature | 299 to 310 | °C | |
| Processing (melt) temperature | 299 to 304 | °C | |
| Mold temperature | 82.2 to 110 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type 1A |
| 4. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |