| LNP THERMOCOMP 9X07435X is a compound based on Miscellaneous resin containing Proprietary Filler(s). Added fature of this grade is: Plateable. Also known as: LNP* THERMOCOMP* Compound 9X07435X Product reorder name: 9X07435X&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | 热塑性聚酯 |
| Material Status | Commercial: Active |
| Features | Electroplating |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.25 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| TD：24 hrs | 1.1 to 1.3 | % | ASTM D955 |
| MD：24 hrs | 0.90 to 1.1 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr，50% RH | 0.098 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 5460 | MPa | ASTM D638 |
| Tensile modulus | 4820 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 51.0 | MPa | ISO 527-2/5 |
| fracture | 59.9 | MPa | ASTM D638 |
| yield | 51.2 | MPa | ISO 527-2/5 |
| yield | 60.1 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.6 | % | ISO 527-2/5 |
| fracture | 1.9 | % | ASTM D638 |
| yield | 1.6 | % | ISO 527-2/5 |
| yield | 1.9 | % | ASTM D638 |
| Bending modulus | 5010 | MPa | ISO 178 |
| 50 mm span | 5350 | MPa | ASTM D790 |
| bending strength | 93.5 | MPa | ISO 178 |
| bending strength | |||
| Fracture, 50 mm span | 95.8 | MPa | ASTM D790 |
| Yield, 50 mm span | 95.3 | MPa | ASTM D790 |
| Fracture bending strain | 2.2 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 3.3 | kJ/m² | ISO 180-1A |
| 23℃ | 35 | J/m | ASTM D256 |
| 23℃ | 270 | J/m | ASTM D4812 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 19 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 111 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 101 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | |||
| 1.00 GHz | 2.90 | ASTM D150 | |
| Dissipation factor | |||
| 1 GHz | 4.7E-3 | ASTM D150 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 93 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 299 to 310 | °C | |
| Barrel middle temperature | 299 to 310 | °C | |
| Barrel front temperature | 299 to 310 | °C | |
| Nozzle temperature | 299 to 310 | °C | |
| Processing (melt) temperature | 299 to 310 | °C | |
| Mold temperature | 107 to 121 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |