| About |
|---|
| LNP THERMOCOMP AF001H is a compound based on ABS resin containing 5% Glass Fiber. Added feature of this material is: Healthcare.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ABS |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 2750 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 40.7 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.3 | % | ASTM D638 |
| Bending modulus | 2740 | MPa | ASTM D790 |
| bending strength | 68.9 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.050 to 0.10 | % | |
| Barrel rear temperature | 204 to 216 | °C | |
| Barrel middle temperature | 232 to 243 | °C | |
| Barrel front temperature | 266 to 277 | °C | |
| Processing (melt) temperature | 260 | °C | |
| Mold temperature | 71 to 82 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type 1A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |