| About |
|---|
| LNP™ THERMOCOMP™ AM, grade name ZF004XXAR1, is a compound based on PPE resin containing 20% glass fiber for Large Format Additive manufacturing (LFAM) applications. PPE based compounds offers lower thermal expansion, improved hydrolytic stability, higher strength to weight ratio and higher temperature performance compared to ABS |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE) |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| XZ direction | 3680 | MPa | |
| ZX direction | 1890 | MPa | |
| Tensile strength | |||
| ZX direction | 21.0 | MPa | |
| XZ direction | 55.0 | MPa | |
| Tensile strain | |||
| XZ direction, fracture | 2.2 | % | |
| ZX direction, fracture | 1.8 | % | |
| Bending stress | 74.0 | MPa | ASTM D6272 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed, 3.2 mm | 131 | ℃ | ASTM D648 |
| Process Conditions | |||
|---|---|---|---|
| Squeezing instructions | Nominal value | Unit | Test method |
| extrusion | Nominal value | Unit | Test method |
| drying temperature | 120 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Temperature of material cylinder zone 1 | 270 to 305 | °C | |
| Temperature of material cylinder zone 2 | 280 to 320 | °C | |
| Temperature of material cylinder zone 3 | 280 to 320 | °C | |
| Temperature of material cylinder zone 4 | 280 to 320 | °C | |
| Melt Temperature | 270 to 305 | °C | |
| Screw length to diameter ratio | 24.0:1.0 | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |