| About |
|---|
| LNP* THERMOCOMP* D351RC compound is based on Polycarbonate resin containing Glass Fiber and Flame Retardant. Added features of this material includes high modulus, good flatness, good impact performance, Non-Halogenated Flame Retardant, PCR content up to 35%. |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.43 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，2.16kg | 27 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：24 hrs | 0.10 to 0.30 | % | |
| TD：24 hrs | 0.10 to 0.30 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 9420 | MPa | ASTM D638 |
| Tensile strength (fracture) | 129 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.2 | % | ASTM D638 |
| Bending modulus | |||
| 50 mm span | 8390 | MPa | ASTM D790 |
| bending strength | |||
| Fracture, 50 mm span | 180 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 130 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 540 | J/m | ASTM D4812 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 119 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 1.9E-5 | 1/℃ | |
| TD：-40~40℃ | 6.9E-5 | 1/℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.80 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 110 | °C | |
| Drying time | 3.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Temperature at the rear of the barrel | 260 to 280 | °C | |
| Temperature in the middle of the barrel | 270 to 290 | °C | |
| Front temperature of material barrel | 280 to 300 | °C | |
| Nozzle temperature | 285 to 305 | °C | |
| Processing (melt) temperature | 285 to 310 | °C | |
| Mold temperature | 80 to 110 | °C | |
| Back pressure | 0.100 to 0.300 | MPa | |
| Screw speed | 50 to 90 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |