| About |
|---|
| LNP THERMOCOMP D551 (or DF00A8P) is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good flatness, good impact performance, Non-Brominated & Non-Chlorinated Flame Retardant.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High impact resistance,Halogen free,Flame Characteristics,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.64 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 300℃，2.16kg | 13 | g/10min | |
| 300℃，5.0kg | 49 | g/10min | |
| Melt Volume Rate | |||
| 300℃，5 kg | 29.5 | cm³/10min | ASTM D1238 |
| Shrinkage rate | ASTM D955 | ||
| MD：24 hrs | 0.050 to 0.20 | % | |
| TD：24 hrs | 0.050 to 0.20 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 15300 | MPa | ASTM D638 |
| — | 15100 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 154 | MPa | ASTM D638 |
| fracture | 153 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 2.1 | % | ASTM D638 |
| fracture | 1.9 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 14900 | MPa | ASTM D790 |
| bending strength | |||
| Fracture, 50 mm span | 223 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 38 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | 130 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 520 | J/m | ASTM D4812 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 21.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 107 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~40℃ | 1.4E-5 | 1/℃ | |
| TD：-40~40℃ | 5.1E-5 | 1/℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.00 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 | °C | |
| Drying time | 3.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 260 to 280 | °C | |
| Barrel middle temperature | 270 to 290 | °C | |
| Barrel front temperature | 280 to 300 | °C | |
| Nozzle temperature | 285 to 305 | °C | |
| Processing (melt) temperature | 285 to 310 | °C | |
| Mold temperature | 80.0 to 110 | °C | |
| Back pressure | 0.100 to 0.300 | MPa | |
| Screw speed | 50 to 90 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 80*10*4 sp=62mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |