| About |
|---|
| DX10311 is 30% glass fiber reinforced, impact modified polycarbonate resin. High flow and good ductility.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High impact resistance,High liquidity,Ductility |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.42 | g/cm³ | ASTM D792 |
| Melt Volume Rate | |||
| 300℃，5 kg | 37.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| MD：3.2 mm | 0.10 to 0.30 | % | |
| TD：3.2 mm | 0.20 to 0.40 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 8340 | MPa | ASTM D638 |
| — | 8260 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 117 | MPa | ASTM D638 |
| fracture | 119 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 2.6 | % | ASTM D638 |
| fracture | 2.7 | % | ISO 527-2/5 |
| Bending modulus | |||
| — | 7670 | MPa | ASTM D790 |
| — | 7730 | MPa | ISO 178 |
| bending strength | |||
| — | 190 | MPa | ASTM D790 |
| — | 182 | MPa | ISO 178 |
| — | 181 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 20 | kJ/m² | ISO 179/2C |
| Charpy Unnotch Impact strength | |||
| 23℃ | 57 | kJ/m² | ISO 179/2U |
| Impact strength of cantilever beam notch | |||
| 23℃ | 200 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 750 | J/m | ASTM D4812 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 128 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~40℃ | 1.9E-5 | 1/℃ | |
| TD：-40~40℃ | 6.4E-5 | 1/℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90.0 to 110 | °C | |
| Drying time | 3.0 to 5.0 | hr | |
| Barrel rear temperature | 250 to 280 | °C | |
| Barrel middle temperature | 280 to 320 | °C | |
| Barrel front temperature | 280 to 320 | °C | |
| Nozzle temperature | 280 to 320 | °C | |
| Processing (melt) temperature | 280 to 320 | °C | |
| Mold temperature | 90.0 to 120 | °C | |
| Back pressure | 1.00 to 5.00 | MPa | |
| Screw speed | 30 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.079 in/min |
| 5. Type 1A |
| 6. at Yield |
| 7. at Break |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |