| About |
|---|
| LNP* Thermocomp* DX15354 compound is a Polycarbonate (PC) compound with improved heat resistance performance, good plating, surface aesthetics and RF performance that makes it a good candidate for internal and external parts for Laser Direct Structuring (LDS) applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Electroplating |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.29 | g/cm³ | ASTM D792 |
| Melt Volume Rate | |||
| 330℃，2.16 kg | 63.0 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.13 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 2920 | MPa | ASTM D638 |
| — | 2940 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 59.0 | MPa | ASTM D638 |
| fracture | 58.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 11 | % | ASTM D638 |
| fracture | 11 | % | ISO 527-2/50 |
| Bending modulus | |||
| — | 2890 | MPa | ASTM D790 |
| — | 2880 | MPa | ISO 178 |
| bending strength | |||
| — | 111 | MPa | ASTM D790 |
| — | 112 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 61 | J/m | ASTM D256 |
| 23℃ | 7.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 2200 | J/m | ASTM D4812 |
| 23℃ | 180 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 168 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 155 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~40℃ | 6.3E-5 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 6.7E-5 | 1/℃ | ASTM E831 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | |||
| 1.10 GHz | 2.95 | Internal Method | |
| Dissipation factor | |||
| 1.1 GHz | 6.0E-3 | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 135 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |