| About |
|---|
| LNP* THERMOCOMP* EC008APQ is a compound based on Polyetherimide containing 40% Carbon Fiber. Added features of this material include: Electrically Conductive, High Flow. FAR25.853 Compliant.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | High liquidity,Conductive |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.44 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 380℃，6.70kg | 40 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| TD：24 hrs | 0.10 to 0.50 | % | ASTM D955 |
| MD：24 hrs | 0.010 to 0.050 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr，50% RH | 0.11 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 6.9 | kJ/m² | ISO 180-1A |
| 23℃ | 64 | J/m | ASTM D256 |
| 23℃ | 560 | J/m | ASTM D4812 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 34 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 7.30 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 193 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-40~150℃ | 4.0E-5 | 1/℃ | ASTM E831 |
| MD：-40~150℃ | 3.0E-6 | 1/℃ | ASTM E831 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 4.5E+2 | ohms | ASTM D257 |
| Volume resistivity | 4.1E+3 | ohms·cm | ASTM D257 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 39400 | MPa | ASTM D638 |
| Tensile modulus | 35500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 268 | MPa | ASTM D638 |
| fracture | 247 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 1.0 | % | ASTM D638 |
| fracture | 0.90 | % | ISO 527-2/5 |
| Bending modulus | 30600 | MPa | ISO 178 |
| 50 mm span | 31300 | MPa | ASTM D790 |
| bending strength | 364 | MPa | ISO 178 |
| Fracture, 50 mm span | 356 | MPa | ASTM D790 |
| compressive strength | 218 | MPa | Internal Method |
| shear modulus | 4660 | MPa | ASTM C273 |
| shear strength | 120 | MPa | ASTM C273 |
| Poisson’s ratio | 0.44 | ASTM D638 | |
| Rockwell hardness | |||
| M-level | 112 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 to 150 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 380 to 400 | °C | |
| Barrel middle temperature | 380 to 400 | °C | |
| Barrel front temperature | 380 to 400 | °C | |
| Processing (melt) temperature | 380 to 400 | °C | |
| Mold temperature | 165 to 180 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |