| About |
|---|
| LNP THERMOCOMP* PF008QS is a compound based on Nylon 6 resin containing 40% Glass Fiber. Added features of this material include: Heat Stabilized, Reduced Moisture.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.35 | g/cm³ | ASTM D792 |
| Density | 1.35 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 0.70 to 0.90 | % | ASTM D955 |
| MD：24 hrs | 0.10 to 0.30 | % | ASTM D955 |
| TD：24 hrs | 0.70 to 0.90 | % | ISO 294-4 |
| MD：24 hrs | 0.10 to 0.30 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.50 | % | ISO 62 |
| 24hr，50% RH | 0.31 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 12200 | MPa | ASTM D638 |
| Tensile modulus | 11600 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 165 | MPa | ISO 527-2 |
| fracture | 152 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.4 | % | ISO 527-2 |
| fracture | 3.0 | % | ASTM D638 |
| Bending modulus | 9580 | MPa | ASTM D790 |
| Bending modulus | 12000 | MPa | ISO 178 |
| bending strength | 245 | MPa | ASTM D790 |
| bending strength | 263 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 18 | kJ/m² | ISO 180-1A |
| 23℃ | 1100 | J/m | ASTM D4812 |
| 23℃ | 170 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 72 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 12.6 | J | ASTM D3763 |
| Multi axial instrumented impact energy | 4.26 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 201 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 199 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 218 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 5.6E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 5.6E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 3.1E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 3.1E-5 | 1/℃ | ISO 11359-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 to 0.25 | % | |
| Barrel rear temperature | 249 to 260 | °C | |
| Barrel middle temperature | 254 to 266 | °C | |
| Barrel front temperature | 266 to 277 | °C | |
| Processing (melt) temperature | 254 to 277 | °C | |
| Mold temperature | 82 to 93 | °C | |
| Back pressure | 0.344 to 0.689 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type 1A |
| 4. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |