| About |
|---|
| LNP THERMOCOMP* RF002XXH is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added feature of this material includes: Healthcare.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| TD：24 hrs | 1.0 to 3.0 | % | ASTM D955 |
| MD：24 hrs | 0.80 to 1.0 | % | ASTM D955 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 1.6 | % | ISO 62 |
| 24hr，50% RH | 0.94 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 4970 | MPa | ASTM D638 |
| Tensile modulus | 5090 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 102 | MPa | ISO 527-2/5 |
| fracture | 87.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.5 | % | ISO 527-2/5 |
| fracture | 2.0 | % | ASTM D638 |
| Bending modulus | 4290 | MPa | ISO 178 |
| 50 mm span | 4620 | MPa | ASTM D790 |
| bending strength | 153 | MPa | ISO 178 |
| Fracture, 50 mm span | 158 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 3.7 | J/m | ASTM D256 |
| 23℃ | 38 | kJ/m² | ISO 180-1A |
| 23℃ | 350 | J/m | ASTM D4812 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 22 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 4.80 | J | ASTM D3763 |
| Multi axial instrumented impact energy | 1.50 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 229 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 239 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 251 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 256 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-30~30℃ | 8.1E-5 | 1/℃ | ASTM D696 |
| MD：-30~30℃ | 5.8E-5 | 1/℃ | ASTM D696 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 to 0.25 | % | |
| Barrel rear temperature | 266 to 277 | °C | |
| Barrel middle temperature | 282 to 293 | °C | |
| Barrel front temperature | 293 to 304 | °C | |
| Processing (melt) temperature | 282 to 304 | °C | |
| Mold temperature | 93 to 110 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |