| About |
|---|
| LNP* THERMOCOMP* RF00CSXP is a compound based on Nylon 66 resin, containing Glass Fiber. Added features of this material include: Heat Stabilized&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA Not specified |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.72 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.10 to 0.30 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.40 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 20000 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 226 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 2.4 | % | ISO 527-2/5 |
| Bending modulus | 17500 | MPa | ISO 178 |
| bending strength | 317 | MPa | ISO 178 |
| Fracture bending strain | 2.7 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 14 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 55 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 64 mm span | 258 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64 mm span | 250 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：23~60℃ | 1.5E-5 | 1/℃ | |
| TD：23~60℃ | 5.3E-5 | 1/℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82.2 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 to 0.25 | % | |
| Barrel rear temperature | 266 to 277 | °C | |
| Barrel middle temperature | 282 to 293 | °C | |
| Barrel front temperature | 293 to 304 | °C | |
| Processing (melt) temperature | 282 to 304 | °C | |
| Mold temperature | 93.3 to 110 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. at Yield |
| 4. 2 mm/min |
| 5. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |