| About |
|---|
| LNP THERMOCOMP* UF0069S is a compound based on Polyphthalamide resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant, Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound UF-1006 FR HS LEX Product reorder name: UF0069S&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Heat Stabilized |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.66 | g/cm³ | ASTM D792 |
| Density | 1.65 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 0.60 | % | ASTM D955 |
| MD：24 hrs | 0.20 | % | ASTM D955 |
| TD：24 hrs | 0.59 | % | ISO 294-4 |
| MD：24 hrs | 0.22 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.26 | % | ISO 62 |
| 24hr，50% RH | 0.24 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 13800 | MPa | ASTM D638 |
| Tensile modulus | 12100 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 182 | MPa | ASTM D638 |
| fracture | 166 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 1.7 | % | ISO 527-2 |
| fracture | 1.9 | % | ASTM D638 |
| Bending modulus | 12100 | MPa | ASTM D790 |
| Bending modulus | 12300 | MPa | ISO 178 |
| bending strength | 258 | MPa | ASTM D790 |
| bending strength | 265 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 550 | J/m | ASTM D4812 |
| 23℃ | 9.0 | kJ/m² | ISO 180-1A |
| 23℃ | 91 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 45 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 2.90 | J | ASTM D3763 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 5VA | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 to 149 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Barrel rear temperature | 282 to 293 | °C | |
| Barrel middle temperature | 288 to 299 | °C | |
| Barrel front temperature | 293 to 304 | °C | |
| Processing (melt) temperature | 299 to 310 | °C | |
| Mold temperature | 138 to 166 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |