| About |
|---|
| LNP THERMOCOMP UF007AS is a compound based on Polyphthalamide resin containing Glass Fiber. Added features include Heat Stabilized .&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.46 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.15 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃，5 mm/min | 194 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃, 5 mm/min | 2.0 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃，1 mm/min | 12100 | MPa | ISO 527-2 |
| bending strength | |||
| Yield, 2 mm/min, 23 ℃ | 279 | MPa | ISO 178 |
| Bending modulus | |||
| 2 mm/min，23℃ | 9600 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 269 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | |||
| MD | 2.20E-5 | 1/℃ | ISO 11359-2 |
| TD | 5.90E-5 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75mm | HB | UL-94 | |
| 3.00mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 11.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 45.0 | kJ/m² | ISO 180/1U |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |