| About |
|---|
| LNP THERMOCOMP UF007SXC is a compound based on Polyphthalamide resin containing Glass Fiber. Added features include : Heat Stabilized .&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.44 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.18 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 11000 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 204 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 2.3 | % | ISO 527-2/5 |
| Bending modulus | 9100 | MPa | ISO 178 |
| bending strength | 280 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 11 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 50 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 258 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：23~60℃ | 2.4E-5 | 1/℃ | |
| TD：23~60℃ | 5.8E-5 | 1/℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Barrel rear temperature | 310 to 321 | °C | |
| Barrel middle temperature | 316 to 327 | °C | |
| Barrel front temperature | 327 to 338 | °C | |
| Processing (melt) temperature | 316 to 332 | °C | |
| Mold temperature | 149 to 171 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |