| About |
|---|
| LNP THERMOCOMP UX06032 is a compound based on Polyphthalamide resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Non-Brominated & Non-Chlorinated Flame Retardant, Heat Stabilized. Custom color white. Also known as: LNP* THERMOCOMP* Compound UX06032-WH9E041 Product reorder name: UX06032-WH9E041&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,Heat Stabilized,V-0 |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.51 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.10 to 0.30 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.50 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 11100 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 93.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 1.5 | % | ISO 527-2/5 |
| Bending modulus | 9600 | MPa | ISO 178 |
| bending strength | 140 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 4.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 20 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 265 | ℃ | ISO 75-2/Af |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 1.5 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 0.8 mm | 825 | ℃ | |
| 1.6 mm | 825 | ℃ | |
| 3 mm | 850 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 3.0 to 5.0 | hr | |
| Barrel rear temperature | 280 to 300 | °C | |
| Barrel middle temperature | 290 to 310 | °C | |
| Barrel front temperature | 295 to 315 | °C | |
| Processing (melt) temperature | 305 to 315 | °C | |
| Mold temperature | 130 to 150 | °C | |
| Back pressure | 0.200 to 0.300 | MPa | |
| Screw speed | 40 to 80 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |