| About |
|---|
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.2 | ASTM D792 | |
| Melt Flow Rate | |||
| 260℃，2.16 kg | 18 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 260℃，2.16 kg | 18 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 0.4-0.5 | % | Internal Method |
| MD | 0.3-0.4 | % | Internal Method |
| Water absorption rate | |||
| 23℃，50% RH | 0.05 | % | ISO 62 |
| Saturation, 23 ℃ | 0.1 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 5 mm/min | 2500 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 63 | MPa | ASTM D638 |
| fracture | 46 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 4 | % | ASTM D638 |
| fracture | 75 | % | ASTM D638 |
| Bending modulus | 2400 | MPa | ASTM D790 |
| bending strength | |||
| yield | 102 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 700 | J/m | ASTM D256 |
| 0℃ | 310 | J/m | ASTM D256 |
| -30℃ | 91 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| B50 | 110 | ℃ | ISO 306 |
| B120 | 116 | ℃ | ISO 306 |
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 92 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 101 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.25 mm | V-2 | UL 94 | |
| 0.6 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80-90 | ℃ | |
| Drying time | 2-4 | hr | |
| Temperature at the rear of the barrel | 230-280 | ℃ | |
| Temperature in the middle of the barrel | 240-260 | ℃ | |
| Front temperature of material barrel | 250-300 | ℃ | |
| Nozzle temperature | 250-300 | ℃ | |
| Processing (melt) temperature | 250-300 | ℃ | |
| Mold temperature | 60-85 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |