| About |
|---|
| LNP THERMOTUF V1000UXC is a compound based on unfilled Super Tough Nylon resin. Added feature of this material is: UV Stabilized.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA Not specified |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Ultra high toughness |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.07 | g/cm³ | ASTM D792 |
| — | 1.08 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：24 hrs | 2.1 to 2.3 | % | ASTM D955 |
| TD：24 hrs | 2.5 to 2.7 | % | ASTM D955 |
| TD：24 hrs | 2.6 | % | ISO 294-4 |
| MD：24 hrs | 2.2 | % | ISO 294-4 |
| Water absorption rate | |||
| 24hr，50% RH | 0.60 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 1.0 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 1710 | MPa | ASTM D638 |
| — | 1650 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 39.0 | MPa | ASTM D638 |
| yield | 41.0 | MPa | ISO 527-2/5 |
| fracture | 39.0 | MPa | ASTM D638 |
| fracture | 41.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 57 | % | ASTM D638 |
| yield | 150 | % | ISO 527-2/5 |
| fracture | 85 | % | ASTM D638 |
| fracture | 170 | % | ISO 527-2/5 |
| Bending modulus | |||
| — | 2070 | MPa | ASTM D790 |
| — | 1700 | MPa | ISO 178 |
| bending strength | |||
| — | 55.2 | MPa | ASTM D790 |
| — | 53.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃ | 无断裂 | ASTM D4812 , ISO 180/1U | |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 49.8 | J | ASTM D3763 |
| — | 49.4 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 192 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 150 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.2 mm | 193 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 147 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 1.4E-4 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 1.3E-4 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 1.3E-4 | 1/℃ | ASTM E831，ISO 11359-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 to 0.25 | % | |
| Barrel rear temperature | 260 to 271 | °C | |
| Barrel middle temperature | 271 to 282 | °C | |
| Barrel front temperature | 288 to 299 | °C | |
| Processing (melt) temperature | 271 to 293 | °C | |
| Mold temperature | 49 to 93 | °C | |
| Back pressure | 0.344 to 0.689 | MPa | |
| Screw speed | 10 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. Type 1A |
| 5. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |