| About |
|---|
| 30% glass fiber reinforced, high metal bonding strength, high flow, for NMT application&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | High liquidity |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.48 | g/cm³ | ASTM D792 |
| Melt Volume Rate | ISO 1133 | ||
| 250℃，5 kg | 14.0 | cm³/10min | |
| 275℃，5 kg | 26.0 | cm³/10min | |
| Shrinkage rate | Internal Method | ||
| MD | 0.12 | % | |
| TD | 0.28 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 7900 | MPa | ASTM D638 |
| — | 8200 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 110 | MPa | ASTM D638 |
| yield | 120 | MPa | ISO 527-2/5 |
| fracture | 110 | MPa | ASTM D638 |
| fracture | 120 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 2.7 | % | ASTM D638 |
| yield | 2.5 | % | ISO 527-2/5 |
| fracture | 2.7 | % | ASTM D638 |
| fracture | 2.5 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 6600 | MPa | ASTM D790 |
| — | 7400 | MPa | ISO 178 |
| bending strength | |||
| — | 166 | MPa | ISO 178 |
| Fracture, 50 mm span | 156 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/2C | ||
| -30℃ | 12 | kJ/m² | |
| 23℃ | 15 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 62 | kJ/m² | ISO 179/2U |
| Impact strength of cantilever beam notch | |||
| -30℃ | 120 | J/m | ASTM D256 |
| 23℃ | 170 | J/m | ASTM D256 |
| -30℃ | 11 | kJ/m² | ISO 180-1A |
| 23℃ | 14 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 840 | J/m | ASTM D4812 |
| 23℃ | 52 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 175 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 158 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 153 | ℃ | ASTM D1525 14 |
| B50 | 157 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 2.1E-5 | 1/℃ | ASTM E831 |
| MD：23~80℃ | 1.5E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 2.2E-5 | 1/℃ | ISO 11359-2 |
| MD：23~80℃ | 1.6E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 7.9E-5 | 1/℃ | ASTM E831 |
| TD：23~80℃ | 4.5E-5 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 8.2E-5 | 1/℃ | ISO 11359-2 |
| TD：23~80℃ | 1.0E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.1E+15 | ohms·cm | ASTM D257 |
| Dielectric constant | Internal Method | ||
| 1.10 GHz | 3.53 | ||
| 1.9 GHz | 3.54 | ||
| Dissipation factor | Internal Method | ||
| 1.1 GHz | 0.012 | ||
| 1.9 GHz | 0.011 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 120 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 40.0 to 60.0 | °C | |
| Barrel rear temperature | 240 to 260 | °C | |
| Barrel middle temperature | 250 to 270 | °C | |
| Barrel front temperature | 250 to 270 | °C | |
| Nozzle temperature | 255 to 275 | °C | |
| Processing (melt) temperature | 250 to 270 | °C | |
| Mold temperature | 100 to 160 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |