| About |
|---|
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High impact resistance,Heat Stabilized,HB |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ISO 294-4 | ||
| 300℃ ，1.2kg | 11 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 11 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD，3.2mm | 0.40~0.50 | % | Internal Method |
| Flow, 3.2mm | 0.20~0.30 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.10 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.030 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 50mm/min | 6300 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, Type I, 50mm/min | 100 | MPa | ASTM D638 |
| fracture | 110 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, Type I, 50mm/min | 3.0 | % | ASTM D638 |
| fracture | 3.0 | % | ISO 527-2/50 |
| Bending modulus | MPa | ||
| 1.3mm/min, 50.0mm span | 5800 | MPa | ASTM D790 |
| 2.0mm/min | 5700 | MPa | ISO 178 |
| bending strength | 228 | MPa | ASTM D790 |
| Yield, 2.0mm/min | 165 | MPa | ISO 178 |
| Yield, 1.3mm/min, 50.0mm | 160 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy notch Impact strength 80 * 10 * 3 sp62mm | |||
| -30℃ | 12 | kJ/m² | ISO 179/1eA |
| 23℃ | 17 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 140 | J/m | ASTM D256 |
| -30℃，80*10*3 | 12 | kJ/m² | ISO 180/1A |
| 23℃，80*10*3mm | 17 | kJ/m² | ISO 180/1A |
| Notched impact strength of cantilever beam | |||
| 23 ℃, total energy | 25.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45MPa, unannealed, 3.20mm span | 135 | ℃ | ASTM D648 |
| 0.45MPa, unannealed, 4.00m, 100mm, 120 * 10 * 4mm | 137 | ℃ | ISO 75-2/Be |
| 1.8MPa, unannealed, 3.20mm | 132 | ℃ | ASTM D648 |
| 1.8MPa, unannealed, 4.00m, 100mm, 120 * 10 * 4mm | 133 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temp | 142 | ℃ | ISO 306/B120 |
| Linear expansion coefficient | |||
| Flow, -40~40 | 2.6E-5 | cm/cm/℃ | ASTM E831 |
| MD，-40~40 | 6.8E-5 | cm/cm/℃ | ASTM E831 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | |||
| 1.10GHz | 3.11 | GHz | ASTMES7-83 |
| 1.90GHz | 3.13 | GHz | Internal Method |
| 5.00GHz | 3.14 | GHz | Internal Method |
| 10.0GHz | 3.16 | GHz | Internal Method |
| Dissipation factor | |||
| 1.10GHz | 6.4E-3 | GHz | ASTMES7-83 |
| 1.90GHz | 6.0E-3 | GHz | Internal Method |
| 5.00GHz | 5.1E-3 | GHz | Internal Method |
| 10.0GHz | 6.3E-3 | GHz | Internal Method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| >0.40mm | HB | UL 94 | |
| >2.0mm | V-1 | UL 94 | |
| >3.0mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 110 | °C | |
| Drying time | 3.0~6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Temperature at the rear of the barrel | 260~280 | °C | |
| Temperature in the middle of the barrel | 270~290 | °C | |
| Front temperature of material barrel | 280~300 | °C | |
| Nozzle temperature | 285~305 | °C | |
| Processing (melt) temperature | 285~310 | °C | |
| Forming temperature | 80~110 | °C | |
| Back pressure | 0.100~0.300 | MPa | |
| Screw speed | 50~90 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |