| About |
|---|
| LNP™ VERTON™ NV004E compound LNP VERTON* NV004E is a compound based on PC+ABS Blend resin containing 20% Long Glass Fiber. Added features of this material include: Easy Molding, Structural. Also known as: LNP* VERTON* Compound PCA-F-7004 EM Product reorder name: NV004E&&LNP™ VERTON™ NV004E compound LNP VERTON* NV004E is a compound based on PC+ABS Blend resin containing Long Glass. Added features of this material include: Easy Molding. Also known as: LNP* VERTON* Compound PCA-F-7004 EM Product reorder name: NV004E&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Excellent Processability |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ASTM D792 |
| Density | 1.30 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 0.20 to 0.40 | % | ASTM D955 |
| MD：24 hrs | 0.20 to 0.40 | % | ASTM D955 |
| TD：24 hrs | 0.20 to 0.40 | % | ISO 294-4 |
| MD：24 hrs | 0.20 to 0.40 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.10 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 6620 | MPa | ASTM D638 |
| Tensile modulus | 7800 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 119 | MPa | ASTM D638 |
| fracture | 125 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.4 | % | ASTM D638 |
| fracture | 2.1 | % | ISO 527-2 |
| Bending modulus | 5670 | MPa | ASTM D790 |
| Bending modulus | 6980 | MPa | ISO 178 |
| bending strength | 160 | MPa | ASTM D790 |
| bending strength | 140 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 23℃ | 570 | J/m | ASTM D4812 |
| -40℃ | 170 | J/m | ASTM D256 |
| 23℃ | 160 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -40℃ | 18 | kJ/m² | ISO 180-1A |
| 23℃ | 18 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 41 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 16.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 134 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 4.8E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 4.7E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 4.5E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 4.3E-5 | 1/℃ | ASTM E831 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 to 93 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Barrel rear temperature | 260 to 271 | °C | |
| Barrel middle temperature | 271 to 282 | °C | |
| Barrel front temperature | 282 to 293 | °C | |
| Processing (melt) temperature | 277 to 288 | °C | |
| Mold temperature | 60 to 93 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |