| About |
|---|
| LNP* Verton* PX0641是以尼龙6为基体和一些填料合成的材料。其优势性能是具有良好的热稳定性。 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good surface appearance,High impact resistance,High liquidity,Antifreeze,Heat Stabilized |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Bending modulus | |||
| 2 mm/mim | 9530 | MPa | ISO 178 |
| 1.3mm/min，跨度50mm | 9996.39 | MPa | ASTM D790 |
| tensile strength | |||
| Fracture, Type I, 5 mm/min | 206 | MPa | ASTM D638 |
| Fracture, 5 mm/min | 182 | MPa | ISO 527 |
| 屈服，5mm/min | 193 | MPa | ISO 527 |
| Tensile strain | |||
| Fracture, Type I, 5 mm/min | 2.5 | % | ASTM D638 |
| Fracture, 5 mm/min | 2.6 | % | ISO 527 |
| Tensile modulus | |||
| 5 mm/min | 11958.39 | MPa | ASTM D638 |
| 1 mm/min | 10900 | MPa | ISO 527 |
| bending strength | 290 | MPa | ISO 178 |
| Fracture, 1.30 mm/min, 50 mm span | 307.053 | MPa | ASTM D790 |
| Yield, 1.30 mm/min, 50 mm span | 309.015 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃，80*10*4 | 64 | kJ/m² | ISO 180/1U |
| 23℃ | 1038.8 | J/m | ASTM D4812 |
| Impact strength of cantilever beam notch | |||
| 23℃，80*10*4 | 27 | kJ/m² | ISO 180-1A |
| 23℃ | 274.4 | J/m | ASTM D256 |
| Multiaxial impact strength | 53 | cm-kgf | ISO 6603 |
| Instrument impact energy | |||
| 23℃ | 156 | cm-kgf | ASTM D 3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 208 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 207 | ℃ | ISO 75/Af |
| 0.45 MPa, unannealed, 64 mm span | 213 | ℃ | ISO 75/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 213 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-30~30℃ | 1.14E-04 | 1/℃ | ASTM D696 |
| MD：-30~30℃ | 4.77E-0.5 | 1/℃ | ASTM D696 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：24 hrs | 0.4-0.6 | % | ASTM D955 |
| MD：24 hrs | 0.1-0.3 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr，50% RH | 1.1 | % | ASTM D570 |
| 23℃，50% RH | 1.7 | % | ISO 62 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Drying temperature | 80 | ℃ | |
| Drying time | 4 | hrs | |
| Maximum absorption capacity | 0.15-0.25 | % | |
| Melt temperature | 265-275 | ℃ | |
| Front temperature | 275-290 | ℃ | |
| Mid section temperature | 265-275 | ℃ | |
| Post stage temperature | 250-260 | ℃ | |
| Mold temperature | 80-95 | ℃ | |
| Back pressure | 0.3-0.7 | MPa | |
| Screw speed | 30-60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |