| About |
|---|
| LNP VERTON RV00CE is a compound based on PA 66 resin containing Long Glass Fiber. Added features include; Easy Molding. Also known as: LNP* VERTON* Compound RF-700-12 EM Product reorder name: RV00CEXP&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Excellent Processability,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.71 | g/cm³ | ISO 1183 |
| Shrinkage rate | Internal Method | ||
| MD | 0.26 | % | Internal Method |
| TD | 0.61 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| 23℃，24hr | 0.90 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 1.1 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 21600 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 270 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 1.7 | % | ISO 527-2/5 |
| Bending modulus | 19000 | MPa | ISO 178 |
| bending strength | 430 | MPa | ISO 178 |
| Fracture bending strain | 2.6 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -40℃ | 43 | kJ/m² | ISO 180-1A |
| 23℃ | 53 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 100 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 64 mm span | 255 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64 mm span | 252 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：23~60℃ | 1.7E-5 | 1/℃ | ISO 11359-2 |
| TD：23~60℃ | 5.3E-5 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 to 0.25 | % | |
| Barrel rear temperature | 282 to 293 | °C | |
| Barrel middle temperature | 288 to 299 | °C | |
| Barrel front temperature | 288 to 299 | °C | |
| Processing (melt) temperature | 288 to 304 | °C | |
| Mold temperature | 93 to 110 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |