| About |
|---|
| LNP VERTON RVL29ESS is a compound based on PA 66 resin, containing Long Glass Fiber, PTFE. Added features include; Internally Lubricated.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Lubricating |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.65 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 0.48 | % | |
| MD：24 hrs | 0.13 | % | |
| Water absorption rate | ISO 62 | ||
| 23℃，24hr | 1.2 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.46 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 231 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 2.3 | % | ISO 527-2/5 |
| Bending modulus | ISO 178 | ||
| — | 13600 | MPa | |
| 60℃ | 11700 | MPa | |
| 100℃ | 10500 | MPa | |
| 150℃ | 9000 | MPa | |
| 200℃ | 8900 | MPa | |
| bending strength | ISO 178 | ||
| — | 361 | MPa | |
| 60℃ | 300 | MPa | |
| 100℃ | 256 | MPa | |
| 150℃ | 204 | MPa | |
| 200℃ | 162 | MPa | |
| friction coefficient | ASTM D3702 Modified | ||
| With oneself – dynamic | 0.39 | ||
| With oneself – static | 0.40 | ||
| Fracture bending strain | ISO 178 | ||
| — | 3.2 | % | |
| 60℃ | 3.6 | % | |
| 100℃ | 3.2 | % | |
| 150℃ | 3.5 | % | |
| 200℃ | 2.7 | % | |
| Wear factor | |||
| Washer | 21.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -40℃ | 28 | kJ/m² | |
| 23℃ | 30 | kJ/m² | |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -40℃ | 74 | kJ/m² | |
| 23℃ | 82 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 258 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：23~60℃ | 2.1E-5 | 1/℃ | |
| TD：23~60℃ | 4.9E-5 | 1/℃ | |
| specific heat | 1480 | J/kg/℃ | ASTM E1269 |
| Thermal conductivity coefficient | 0.27 | W/m/K | ASTM D5930 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82.2 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 to 0.25 | % | |
| Barrel rear temperature | 282 to 293 | °C | |
| Barrel middle temperature | 288 to 299 | °C | |
| Barrel front temperature | 288 to 299 | °C | |
| Processing (melt) temperature | 288 to 304 | °C | |
| Mold temperature | 93.3 to 110 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. at Yield |
| 4. 2 mm/min |
| 5. Modified: Manual |
| 6. 80*10*3 mm |
| 7. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |