| LNP* Verton* UX0645是基于含有长玻璃纤维的聚邻苯二甲酰胺树脂的化合物。 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Low or no water absorption,Good Hardness,High Heat Resistance |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| impact strength | Nominal value | Unit | Test method |
| Multiaxial impact | 142 | cm-kgf | ISO 6603 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 3.2E-05 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 2.2E-05 | 1/℃ | ISO 11359-2 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shrinkage rate | |||
| MD：24 hrs | 0.2 | % | ISO 294 |
| MD：24 hrs | 0.06 | % | ISO 294 |
| Density | 1.63 | g/cm³ | ISO 1183 |
| Density | 1.63 | g/cm³ | ASTM D792 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃，80*10*4 | 75 | kJ/m² | ISO 180/1U |
| 23℃ | 1489.6 | J/m | ASTM D4812 |
| Impact strength of cantilever beam notch | |||
| 23℃，80*10*4 | 40 | kJ/m² | ISO 180-1A |
| 23℃ | 401.8 | J/m | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 275 | MPa | ISO 527 |
| fracture | 279 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.7 | % | ISO 527 |
| fracture | 1.9 | % | ASTM D638 |
| Tensile modulus | |||
| 50 mm/min | 19306.08 | MPa | ASTM D638 |
| 1 mm/min | 19000 | MPa | ISO 527 |
| bending strength | 375 | MPa | ISO 178 |
| Bending modulus | 17400 | MPa | ISO 178 |
| Water absorption rate | |||
| 24hr，50% RH | 0.3 | % | ASTM D570 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Drying temperature | 120-150 | ℃ | |
| Drying time | 4 | hrs | |
| Maximum water content | 0.15 | % | |
| Melt temperature | 315-330 | ℃ | |
| Front temperature | 330-345 | ℃ | |
| Mid section temperature | 320-330 | ℃ | |
| Post stage temperature | 315-325 | ℃ | |
| Mold temperature | 140-165 | ℃ | |
| Back pressure | 0.2-0.3 | MPa | |
| Screw speed | 30-60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |