| PBT 3030-200S is a 30% glass fiber reinforced natural color injection molding grade.&& |
| Product Description | |
|---|---|
| Supplier | Chang Chun |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.50 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.8-1.1 | % | ISO 294-4 |
| TD | 0.1-0.3 | % | ISO 294-4 |
| Melt Flow Rate | |||
| 250℃，2.16kg | 9 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 120 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 9000 | MPa | ISO 527-2 |
| bending strength | |||
| 23℃ | 180 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 7000 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 210 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, annealed | 200 | ℃ | ISO 75-2/Af |
| Melting temperature | 225 | ℃ | ISO 11357-3 |
| Vicat Softening Temp |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+15 | Ω.cm | IEC 60093 |
| Surface resistance | 1.0E+13 | Ω.cm | IEC 60093 |
| Insulation strength | |||
| 2.00mm | 24 | KV/mm | IEC 60243-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 14 | kJ/m² | ISO 179/1eA |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 -140 | °C | |
| Drying time | 4 | Hr | |
| Injection temperature | |||
| Barrel front temperature | 240-270 | °C | |
| Mold temperature | 60-100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |