| About |
|---|
| PBT 4830- BKF是30%玻璃纤维增强,阻燃,注射成型等级 |
| Product Description | |
|---|---|
| Supplier | Chang Chun |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Good wear resistance,Solvent resistance,Glass fiber reinforced,V-0 |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.63 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 100 | Mpa | ASTM D638 |
| Tensile strain | 3.2 | % | ASTM D638 |
| bending strength | 170 | MPa | ASTM D790 |
| Bending modulus | 8500 | MPa | ASTM D790 |
| Rockwell hardness |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 220 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 205 | ℃ | ISO 75-2/A |
| melting point | 225 | ℃ | ISO 11357-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 2 mm | 22 | KV/mm | IEC 60243 |
| Volume resistivity | 10^15 | ohms·cm | IEC 60293 |
| Surface resistivity | 1E+13 | ohms | IEC 60293 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | kJ/m² | ASTM D256 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Drying temperature | 120-140 | °C | |
| Drying time | 4 | Hr | |
| Processing temperature | 240-270 | °C | |
| Mold temperature | 60-100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |