| PMC-T310 Black Phenolic is a two-stage, mechanical purpose molding material offering excellent mold process-ability and optimized Cure cycles. Typical applications include automotive interior parts, circuit breaker and drive train component, etc.&& |
| Product Description | |
|---|---|
| Supplier | Chang Chun |
| Generic | 酚醛树脂 |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Electrical Properties,Fast Cure,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.53 | g/cm³ | ASTM D792 |
| Density | 1.53 | g/cm³ | JIS K7112 |
| Shrinkage rate | |||
| — | 8.0 | % | JIS K6915 |
| — | 8.0 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.15 | % | ASTM D570 |
| 23℃，24hr | 0.15 | % | JIS K6911 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 56.0 | MPa | ASTM D638 |
| tensile strength | 56.0 | MPa | JIS K6911 |
| bending strength | 125 | MPa | ASTM D790 |
| bending strength | 125 | MPa | JIS K7203 |
| compressive strength | 220 | MPa | ASTM D695 |
| compressive strength | 220 | MPa | JIS K6911 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy impact strength | |||
| — | 4.4 | kN/m | ASTM D256 |
| — | 4.4 | kN/m | JIS K7111 |
| Izod notched impact strength | |||
| — | 3.7 | kN/m | ASTM D256 |
| — | 3.7 | kN/m | JIS K6911 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 190 | ℃ | JIS K7207 |
| 1.8 MPa, unannealed | 190 | ℃ | ASTM D648 |
| Relative temperature index | |||
| Electrical performance | 150 | ℃ | UL 746 |
| Strength mechanical performance | 150 | ℃ | UL 746 |
| Impact mechanical performance | 150 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+13 | ohms·cm | ASTM D257 |
| Volume resistivity | 1.0E+13 | ohms·cm | JIS K6911 |
| Dielectric strength | |||
| — | 14 | kV/mm | ASTM D149 |
| — | 14 | kV/mm | JIS K6915 |
| Arc resistance | PLC 5 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 4 | UL 746 | |
| insulation resistance | |||
| — | 1.0E+11 | ohms | ASTM D257 |
| — | 1.0E+11 | ohms | JIS K6915 |
| — | 1.0E+9 | ohms | ASTM D257 |
| — | 1.0E+9 | ohms | JIS K6915 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 3.00 mm | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Storage period | 12 | month |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. (N) |
| 3. (B) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |