| PMC-T375J Black Phenolic is a two-stage, heat resistant/electrical molding material offering excellent mold process-ability and optimized Cure cycles. Typical applications include circuit breaker, transformer part , telecommunication application, etc.&& |
| Product Description | |
|---|---|
| Supplier | Chang Chun |
| Material Status | Commercial: Active |
| Features | V-0,Fast Cure,Excellent Processability,Good Electrical Properties,Heat Resistance, Good |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.52 | g/cm³ | ASTM D792 |
| Density | 1.52 | g/cm³ | JIS K7112 |
| Molding shrinkage | |||
| — | 9.5 | % | JIS K6915 |
| — | 9.5 | % | ASTM D955 |
| Water Absorption | |||
| 24hr | 0.18 | % | ASTM D570 |
| 23℃，24hr | 0.18 | % | JIS K6911 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | 50.0 | MPa | ASTM D638 |
| Tensile Strength | 50.0 | MPa | JIS K6911 |
| Flexural Strength | 90.0 | MPa | ASTM D790 |
| Flexural Strength | 90.0 | MPa | JIS K7203 |
| Compressive Strength | 190 | MPa | ASTM D695 |
| Compressive Strength | 190 | MPa | JIS K6911 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Impact strength of simply supported beams | |||
| — | 2.9 | kN/m | ASTM D256 |
| — | 2.9 | kN/m | JIS K7111 |
| Izod Impact strength of cantilever beam | |||
| — | 2.5 | kN/m | ASTM D256 |
| — | 2.5 | kN/m | JIS K6911 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 180 | ℃ | JIS K7207 | |
| 1.8 MPa, unannealed | 180 | ℃ | ASTM D648 |
| Relative Temperature Index (RTI) | |||
| 150 | ℃ | UL 746 | |
| Strength mechanical performance | 150 | ℃ | UL 746 |
| Impact mechanical performance | 150 | ℃ | UL 746 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | 1.0E+12 | ohms·cm | ASTM D257 |
| Volume Resistance | 1.0E+12 | ohms·cm | JIS K6911 |
| Dielectric Strength | |||
| — | 13 | kV/mm | ASTM D149 |
| — | 13 | kV/mm | JIS K6915 |
| Arc Resistance | PLC 5 | ASTM D495 | |
| Compared Tracking Index | PLC 3 | UL 746 | |
| Insulation resistance | |||
| — | 1.0E+10 | ohms | ASTM D257 |
| — | 1.0E+10 | ohms | JIS K6915 |
| — | 1.0E+8 | ohms | ASTM D257 |
| — | 1.0E+8 | ohms | JIS K6915 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.45 mm | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Storage period | 12 | month |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. (N) |
| 3. (B) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |