| LONOY lonoy 3010是一种聚碳酸酯+聚丁烯对苯二甲酸酯（PC+PBT）材料,含有的填充物为玻璃纤维增强材料。 该产品在北美洲或亚太地区有供货,加工方式为:注射成型。 LONOY lonoy 3010的主要特性有: 阻燃/额定火焰 美观 耐候性好 典型应用领域包括: 电气/电子应用 工具 家庭应用 商业/办公用品&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good surface appearance,Good coloring,HB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：23℃ | 0.40 to 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.20 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 180 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃，3.2 mm | 700 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 140 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 125 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 1.6 mm | 30 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 95 | ASTM D785 | |
| tensile strength | 75.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 10 | % | ASTM D638 |
| Bending modulus | 3600 | MPa | ASTM D790 |
| bending strength | 110 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 245 to 260 | °C | |
| Barrel middle temperature | 250 to 270 | °C | |
| Barrel front temperature | 250 to 270 | °C | |
| Processing (melt) temperature | 245 to 270 | °C | |
| Mold temperature | 70 to 90 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |