| LOTADER® 6200 is a random terpolymer of ethylene, acrylic ester and maleic anhydride, polymerized by high-pressure autoclave process. Applications Due to its properties, reactivity, fluidity and compatibility with tackifying resins and waxes, LOTADER® 6200 is suitable as additive for hot melt adhesive formulations and as coupling agent in mineral filled compounds.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | EEA |
| Material Status | Commercial: Active |
| Features | Good liquidity,Terpolymer,Heat Stabilized,High reactivity |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.940 | g/cm³ | ASTM D1505 |
| Density | 0.940 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 40 | g/10min | ISO 1133 |
| 190℃，2.16kg | 40 | g/10min | ASTM D1238 |
| Ethyl acrylate content | 6.5 | wt% | |
| Maleic anhydride content | 2.8 | wt% | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 36 | ASTM D2240 | |
| Shaw’s D, molded | 36 | ISO 868 | |
| tensile strength | |||
| Fracture, molded | 6.00 | MPa | ASTM D638 |
| Fracture, molded | 6.00 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, molded | 600 | % | ASTM D638 |
| Fracture, molded | 600 | % | ISO 527-2 |
| Bending modulus | |||
| Compression Molding | 95.0 | MPa | ISO 178 |
| Compression Molding | 95.0 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 66.0 | ℃ | ASTM D1525 2 |
| Vicat Softening Temp | 66.0 | ℃ | ISO 306/A |
| Melting temperature | 102 | ℃ | ISO 11357-3 |
| Ring and Ball Softening Point | 119 | ℃ | ASTM E28 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |